Welding of 18%Cr-8%Ni austenitic STS(AISI 304, 304L, 304LN, ASTM A157 Gr. C9; A320 Gr. B8C or D)
- K-308LT is designed for MAG welding of low carbon 18%Cr - 8%Ni stainless steel and used to joint austenitic stainless steel (AISI 304, 304L, 304LN, ASTM A157 Gr. C9; A320 Gr. B8C or D)
- The weld metal contains optimum ferrite contents in their austenitic structures, Therefore their weldability is excellent with lower crack susceptibility.
- It has easy slag removal, low spatter generation and good weld soundness of weld metal.
Typical chemical composition of wire (%)
|
Carbon |
Sulphur |
Silicon |
Manganese |
Phosphorus |
|
0,03 % |
- |
0,60 % |
1,20 % |
- |
100% CO?(15~25?/min), Ar+20% CO? (15~25?/min)
KS : D3612 : YF-308LC
AWS : A5.22 : E308LT1-1/4
EN : ISO 17633-A : T 19 9 L P C(M) 1
EN : ISO 17633-B : TS308L-FB1
JIS ; Z3323 : TS308L-FB1
Key Features
| Sizes (mm) | Standard | Welding Position View(+) |
Shielding gas | Polarity | |
|---|---|---|---|---|---|
| 1.2~1.6 | AWS A5.22 JIS Z3323 KS D3612 EN ISO 17633-A EN ISO 17633-B |
E308LT1-1/4 TS308L-FB1 YF-308LC T 19 9 L P C(M) 1 TS308L-FB1 |
F, HF, H, VU, VD, OH | CO2 / Ar+20%CO2 | DC(+) |
| Typical chemical composition all-weld metal (%) | ||||||||
|---|---|---|---|---|---|---|---|---|
| C | Si | Mn | P | S | Cr | Ni | Mo | Remark |
| 0.03 | 0.60 | 1.20 | - | - | 20.30 | 10.50 | - | FN 3~8 및 8~12 |
| Typical mechanical properties of all-weld metal | |||||
|---|---|---|---|---|---|
| Y.S (MPa) | T.S (MPa) | EI. (%) | Hardness (HV) | IV (J) | PWHT |
| 440 | 570 | 39 | - | 65 (-40℃) | - |